WHAT IS OPTIFORM®?
OptiForm® are the family of plug aid materials developed by CGP Europe to combine the durability of engineering thermoplastics with the low thermal conductivity of a syntactic foam. OptiForm® Plug assists will reduce the staining and adhesion of difficult-to-process polymers while resisting the chips and knocks associated with manufacturing misuse. OptiForm® Materials retain the high thermal stability required to process today's thermoformed polymers. In addition, OptiForm® Materials eliminates the processing difficulties of traditional syntactic foams.
OVERVIEW
OptiForm B2X is a sealing aid that combines the toughness of engineering thermoplastics with the low thermal conductivity of a syntactic foam.OptiForm B2X will reduce the staining and adhesion of difficult-to-process polymers while reducing the staining and adhesion of difficult-to-machine polymers, while the OptiForm B2X will provide the best smooth surface finish. gives.
TECHNICIAL SPECIFICATIONS
Color: Blue
Density (p) 44 -48 lb / ft³ 710 -770 kg / m³
Thermal Conductivity (k) 0.086 BTU / hr-ft- ° F 0.18 W / m ° K
Specific Heat (Cp) per mass 0.43 BTU / (lb ° F) 1.80 kJ / (kg ° C)
Coef. Therm. Expansion (CTE) 33 x 10-6 in / in / ° F 60 x 10-6 m / m / ° C
Compressive Strength 9,700 psi 70 Mpa
Service Temperature 356 ° F 180 ° C
BENEFITS
STANDARD DIMENSIONS
High Toughness and Durability
With high toughness, machine downtime due to damaged plugs is reduced. Less downtime, lower cost, more consistent quality
to.
Superior Machinability
Dust collection equipment or respirators are not required due to large, non-corrosive chips. Thanks to the easy chip formation, chips can be processed three times faster than syntactic foam.
No more complaints from their machinists.
Excellent Temperature Resistance
OptiForm B2X has been specially formulated for service up to 180 ° C with minimal loss of mechanical properties.
OPTICUT 
APPS
OptiForm B2X can be used in a wide variety of applications in sheet-fed, rotary or in-line machines. It can also be used most commonly with thermoformed materials and has proven to be highly effective with polypropylene and other polyolefins.
With PP, PET and PLA we will achieve better productivity than other epoxy syntaxes.OptiForm B2X is ready to replace other thermoplastic syntactic materials such as Hytac® B1X.
OVERVIEW
OptiForm F2X is the plug aid that combines the following. Low toughness of engineering thermoplastics syntactic thermal conductivity of a foam. Plug supports made from OPTIFORM F2X will reduce the staining and adhesion of difficult-to-process polymers while resisting chips and knocks associated with the abuse of manufacturing.OptiForm F2X eliminates the processing difficulties of conventional syntactic foams.
This product does not generate dust during the processing and finishing of the plugs.
TECHNICIAL SPECIFICATIONS
Color: White
Density (p) 43 -47 lb / ft³ 700 -760 kg / m³
Thermal Conductivity (k) 0,092 BTU / hr-ft- ° F 0.17 W / m ° K
Specific Heat (Cp) per mass 0.43 BTU / (lb ° F) 1.80 kJ / (kg ° C)
Coef. Therm. Expansion (CTE) 33 x 10-6 in / in / ° F 60 x 10-6 m / m / ° C
Compressive Strength 9,700 psi 67 Mpa
Service Temperature 356 ° F 180 ° C
BENEFITS
STANDARD DIMENSIONS
High Toughness and Durability
With high toughness, machine downtime due to damaged plugs is reduced. Less downtime, lower cost, more consistent quality.
Superior Machinability
Dust collection equipment or respirators are not required due to large, non-corrosive chips. Thanks to the easy chip formation, chips can be processed three times faster than syntactic foam.
No more complaints from their machinists.
Excellent Temperature Resistance
OptiForm B2X has been specially formulated for service up to 180 ° C with minimal loss of mechanical properties.
OPTICUT
APPS
The OptiForm F2X can be used in a wide variety of applications in sheet-fed, rotary or in-line machines. It can also be used most commonly with thermoformed materials and has proven effectiveness with PS, PVC and PET.
OptiForm F2X is ready to replace epoxy-based Hytac® or Syntac® to prevent dusty processing!
OVERVIEW
OptiForm FXT is a plug auxiliary material that combines the durability of engineering thermoplastics with the low thermal conductivity of a syntactic foam.OptiForm FXT eliminates processing dust compared to standard syntactic green material. The formulation will minimize plug / sheet friction and the best material thickness for multilayer film It is designed to provide distribution.
OptiForm FXT provides a very smooth surface.
TECHNICIAL SPECIFICATIONS
Color: Green
Density (p) 790 -830 kg / m³
Thermal Conductivity (k) 0.17 W / m ° K
Coef. Therm. Expansion (CTE) 59 x 10-6 m / m / ° C
Compressive Strength 73 Mpa
Compressive Modulus 2.0 Gpa
Service Temperature 180 ° C
BENEFITS
STANDARD DIMENSIONS
High Toughness and Durability
With high toughness, machine downtime due to damaged plugs is reduced. Less downtime, lower cost, more consistent quality.
Superior Machinability
Dust collection equipment or respirators are not required due to large, non-corrosive chips. Thanks to the easy chip formation, chips can be processed three times faster than syntactic foam.
No more complaints from their machinists.
Perfect Sheet Release
OptiForm FXT is specially formulated with PTFE to reduce the coefficient of friction between plug and plate.
OPTICUT
APPS
OptiForm FXT can be used in a wide variety of applications in sheet-fed, rotary or in-line machines. Also, the mostIt can also be used with commonly thermoformed materials, but is special for Multilayer. OptiForm FXT, Ready to replace other materials such as Hytac® FLXT and WFT
OVERVIEW
OptiForm® SLX is a occlusion aid material that combines the durability of engineering thermoplastics with the low thermal conductivity of a syntactic foam.OptiForm® SLX eliminates processing dust compared to the standard FLX material, but with a similar finish. The formulation provides the best thickness distribution and high transparency. OptiForm® SLX provides a very smooth final surface, minimizing the cooling of the sheet and improving the plug / sheet interaction.
OptiForm® materials are DUST FREE during processing, finishing and cutting.
TECHNICIAL SPECIFICATIONS
Color: Pink Salmon
Density (p) 780 -820 kg / m³
Thermal Conductivity (k) 0.16 W / m ° K
Coef. Therm. Expansion (CTE) 55 x 10-6 m / m / ° C
Compressive Strength 70 Mpa
Compressive Modulus 2.10 Gpa
Service Temperature 180 ° C
BENEFITS
STANDARD DIMENSIONS
High Toughness and Durability
With high toughness, machine downtime due to damaged plugs is reduced. Less downtime, lower cost, more consistent quality.
Superior Machinability
Dust collection equipment or respirators are not required due to large, non-corrosive chips. Stoppers can be processed three times faster than copolymer or epoxy syntactic foam due to easy chip formation.
No more complaints from their machinists.
Excellent Temperature Resistance
OptiForm® SLX has been specially formulated for service up to 180 ° C with minimal loss of mechanical properties.
OPTICUT
APPS
OptiForm® SLX can be used in a wide variety of applications in sheet-fed, rotary or in-line machines. It can also be used most commonly with thermoformed materials and has proven to be highly effective with polypropylene and other polyolefins.
We will achieve better productivity with PET and PP than with other epoxy syntaxes.
OptiForm® SLX is ready to replace other materials such as Hytac® FLX.
Contact
RENAT GLOBAL İNŞ. İHR. İTH. SAN. ve TİC. LTD. ŞTİ.
Bahcelievler Mah. 193.Sk. No: 1/4 PK10050. Altıeylül / Balikesir / TURKEY
E-Mail: info@renatglobal.com
Tel (TR): +90 542 492 63 32
Tel-Whatsapp (DE): +49 179 929 444 12